COLD FORMING TOOLING MATERIALS CHEMISTRIES & PROPERTIES |
|
|
AISI |
GRADE NAME |
C
|
Cr
|
V
|
Mo
|
W
|
OTHER
|
WEAR RESISTANCE
|
TOUGHNESS
|
|
|
L6 |
CHAMPALOY |
0.75
|
0.80
|
|
0.30
|
|
1.50 Ni
|
|
|
|
O1 |
KETOS |
0.90
|
0.50
|
|
|
0.50
|
|
|
|
|
O6 |
HALGRAPH |
1.50
|
|
|
0.25
|
|
|
|
|
|
S5 |
LABELLE SIL #2 |
0.60
|
0.25
|
0.20
|
0.30
|
|
1.90 Si
|
|
|
|
A9 |
CRUCIBLE A9 |
0.50
|
5.20
|
1.00
|
1.40
|
|
1.40 Ni
|
|
|
|
S7 |
CRUCIBLE S7 |
0.55
|
3.25
|
0.25
|
1.40
|
|
|
|
|
|
S7 PREM |
CRUCIBLE S7 XL |
0.55
|
3.25
|
0.25
|
1.40
|
|
0.005 S max
|
|
|
|
A6 |
CSM 6 |
0.70
|
1.00
|
|
1.35
|
|
2.00 Mn
|
|
|
|
A2 (S) |
AIRKOOL (S) |
1.00
|
5.25
|
0.25
|
1.10
|
|
|
|
|
|
|
CPM 1V |
0.55
|
4.50
|
1.00
|
2.75
|
2.15
|
|
|
|
|
D2 (S) |
AIRDI 150 (S) |
1.55
|
11.50
|
0.90
|
0.80
|
|
|
|
|
|
|
CRU-WEAR |
1.10
|
7.50
|
2.40
|
1.60
|
1.15
|
|
|
|
|
|
CPM 3V |
0.80
|
7.50
|
2.75
|
1.30
|
|
|
|
|
|
M2 |
REX M2 (S) |
0.85
|
4.15
|
2.00
|
5.00
|
6.40
|
|
|
|
|
M4 |
CPM M4HC(HS) |
1.40
|
4.00
|
4.00
|
5.25
|
5.50
|
|
|
|
|
|
CPM 9V |
1.80
|
5.25
|
9.00
|
1.30
|
|
|
|
|
|
T15 |
CPM T15 |
1.60
|
4.00
|
4.90
|
|
12.00
|
5.00 Co
|
|
|
|
A11 |
CPM 10V |
2.45
|
5.25
|
9.75
|
1.30
|
|
|
|
|
|
|
CPM 15V |
3.40
|
5.25
|
14.50
|
1.30
|
|
|
|
|
|
4140 MOD |
MAXEL TOOLING ALLOY |
0.42
|
1.00
|
|
0.20
|
|
|
|
|
|
52100 |
52100 |
1.00
|
1.50
|
|
|
|
|
|
|
|
NOTE: ALL WEAR RESISTANCE AND TOUGHNESS DATA IS NOMINALLY RELATIVE AT HRC 58/61 WITH THE EXCEPTION OF 4140 (HRC 28/32) AND CPM 9V (HRC 53/55). |
|